  1. The austenitic chromium-nickel stainless steels are cold formed (bent,
  2. drawn, shaped) and the cold forming imparts a higher strength than for the
  3. original starting annealed condition.  It is not typical to heat these
  4. stainless steels for forming as is often done with carbon steel.  The
  5. following are the designations of cold worked tempers as defined by ASTM
  6. A 666, Standard Specification for Austenitic Stainless Steel, Sheet, 
  7. Strip, Plate & Flat Bar.
  8.  
  9.      1/4 Hard, 1/2 Hard, 3/4 Hard, Full Hard
  10.  
  11.  
  12. Reheating the cold worked austenitic stainless steels at temperatures 
  13.  below 370C (700F) increases the tensile strength.  Reheating above 425C 
  14.  (900F) lowers the strength and increases the ductility.
  15.  
  16. Cold working increases the fatigue strength of the austenitic stainless
  17.  steels.  However, the fatigue strength of these cold worked alloys is 
  18.  reduced by notches, as compared to notched fatigue strength in the 
  19.  annealed condition.
  20.  
  21.  Fatigue Strength (Endurance Limits) of Cold Worked Stainless Steels:
  22.  
  23. AISI Type      Temper       Endurance Limit - ksi
  24.  
  25. 301            Full Hard            80
  26. 302            Full Hard            75
  27. 303            1/4 Hard             48
  28. 304            Annealed             35  
  29. 304            1/2 Hard             70
  30. 304            3/4 Hard             92
  31. 347            3/4 Hard             88
  32.  
  33.  
  34. Minimum Tensile Strength of Cold Rolled Sheet & Strip for 304
  35.  
  36.      The other common 300 series alloys are similar.
  37.  
  38.                                                     Rockwell C
  39.   Temper        Tensile ksi   Yield ksi   Elong. %  Hardness
  40.  
  41.  1/4 Hard          125           75         23         25
  42.  1/2 Hard          150          110         16         32
  43.  3/4 Hard          175          135         11         37
  44.  Full Hard         185          140          8         41
  45.  Extra Full Hard   200            -          -         45
  46.  
  47.  
  48. Tensile Strength of Cold Drawn Cr-Ni Stainless Steel Wire
  49. Diameter Range of 0.126 - 0.375"
  50.  
  51. AISI  TYPE     TEMPER      YIELD-ksi   TENSILE-ksi  ELONG.%
  52.  
  53.  302          1/4 hard       90-125     120-140      15-25
  54.               1/2 hard      120-150     145-176      10-17
  55.               3/4 hard      150-180     170-200       5-10
  56.             * Full hard     180-220     190-230       2-5
  57.     
  58.     * Typical of wires used in making stranded wire rope 
  59.  
  60.  304          1/4 hard       90-110     120-140      20-30
  61.               1/2 hard      120-140     130-170      10-18
  62.               3/4 hard      140-170     170-200       5-10
  63.               Full hard     170-210     200-240       2-5
  64.  
  65.  309S         1/4 hard       80-90      110-130      15-25
  66.               1/2 hard      105-125     125-155      10-11
  67.               3/4 hard      125-150     140-180       8-12
  68.               Full hard     150-185     160-190       4-8
  69.  
  70.  310S         1/4 hard       80-90      110-130      15-25
  71.               1/2 hard      105-125     125-155      10-11
  72.               3/4 hard      125-150     140-180       8-12
  73.               Full hard     150-185     160-195       4-8
  74.  
  75.  316          1/4 hard       80-100     110-130      20-30
  76.               1/2 hard      105-125     135-155      12-20
  77.               3/4 hard      135-165     165-195       8-12
  78.               Full hard     155-185     185-215       3-6
  79.  
  80.  321          1/4 hard       90-110       120-140      20-30
  81.               1/2 hard      120-140     150-170      10-18
  82.               3/4 hard      140-170     170-200       5-10
  83.               Full Hard     170-210     200-240       2-5
  84.  
  85.  347          1/4 hard       85-105     115-135      15-25
  86.               1/2 hard      110-130     140-160      10-13
  87.               3/4 hard      140-170     170-200       5-10
  88.               Full hard     160-190     190-220       3-6
  89.  
  90.  
  91.  
  92. TENSILE PROPERTIES OF AUSTENITIC STAINLESS STEELS
  93. FOR VARIOUS AMOUNTS OF COLD WORKING
  94.  
  95.                 STRENGTH IN ksi for % COLD REDUCTION SHOWN
  96. ALLOY     0      10%      20%     30%     40%     50%     60%
  97.  
  98.  301
  99. Tensile  120     150      168     184     198     210     222
  100. Yield    40      87       120     148     170     185     202
  101. Elong.   75%     58%      42%     32%     22%     15%     6%
  102.  
  103.  302
  104. Tensile  93      108      122     138     152     168     180
  105. Yield    37      91       107     120     134     147     160
  106. Elong.   67%     42%      30%     20%     15%     10%     6%
  107.  
  108.  303
  109. Tensile  91      106      125     148     171     196      -
  110. Yield    No data
  111. Elong.   63%     47%      29%     19%     15%     12%      -
  112.  
  113.  304
  114. Tensile  86      98       113     130     146     158     169
  115. Yield    34      69       97      120     135     145     152
  116. Elong.   53%     36%      25%     16%     13%     10%     6%
  117.  
  118.  304L
  119. Tensile  83      106      122     138     154     170      -
  120. Yield    32      72       97      120     138     152      -
  121. Elong.   57%     35%      23%     15%     10%     5%       -
  122.  
  123.  309S
  124. Tensile  80      87       98      115     135     151     165
  125. Yield    37      57       82      102     122     140     153
  126. Elong.   55%     45%      30%     14%     9%      5%      3%
  127.  
  128.  310S
  129. Tensile  86      108      126     140     153     166     174
  130. Yield    45      67       97      125     140     148     152
  131. Elong.   45%     29%      15%     8%      6%      5%      5%
  132.  
  133.  316
  134. Tensile  85      95       110     130     142     150     169
  135. Yield    38      70       98      118     128     137     148
  136. Elong.   60%     40%      21%     12%     8%      6%      5%
  137.  
  138.  321
  139. Tensile  88      100      115     135     150     160     168
  140. Yield    32      70       100     120     134     142     145
  141. Elong.   55%     45%      26%     13%     8%      5%      4%
  142.  
  143.  347
  144. Tensile  96      105      122     144     159     168     173