  1.  201     .15  6.50 .060 .030  1.00  17.00   4.50        0.25 N
  2.  202     .15  9.00 .060 .030  1.00  18.00   5.00        0.25 N
  3.  301     .15  2.00 .045 .030  1.00  17.00   7.00       
  4.  302     .15  2.00 .045 .030  1.00  18.00   9.00       
  5.  303     .15  2.00 .200 .150  1.00  18.00   9.00  0.60 
  6.  303Se   .15  2.00 .200 .060  1.00  18.00   9.00        0.15 Se
  7.  304     .08  2.00 .045 .030  1.00  19.00   9.25       
  8.  304L    .03  2.00 .045 .030  1.00  19.00  10.00       
  9.  309S    .08  2.00 .045 .030  0.75  23.00  13.50       
  10.  310S    .08  2.00 .045 .030  1.50  25.00  20.50       
  11.  316     .08  2.00 .045 .030  1.00  17.00  12.00  2.50 
  12.  316L    .03  2.00 .045 .030  1.00  17.00  12.00  2.50 
  13.  317     .08  2.00 .045 .030  1.00  19.00  13.00  3.50 
  14.  317L    .03  2.00 .045 .030  1.00  19.00  13.50  3.50  
  15.  321     .08  2.00 .045 .030  1.00  18.00  10.50        Ti 5 x C
  16.  329     .10  2.00 .045 .030  1.00  27.50   4.50  1.50 
  17.  330     .08  2.00 .040 .030  1.00  18.50  35.50       
  18.  347     .08  2.00 .045 .030  1.00  18.00  11.00        Cb + Ta  10 x C
  19.  409     .08  1.00 .045 .045  1.00  11.15               Ti 6 x C
  20.  410     .15  1.00 .040 .030  1.00  12.50              
  21.  416     .15  1.25 .040       1.00  13.00         0.60  S is .15 min
  22.  416Se   .15  1.25 .060 .060  1.00  13.00               0.15 Se
  23.  420     .15  1.00 .040 .030  1.00  13.00              
  24.  430     .12  1.00 .040 .030  1.00  17.00              
  25.  440C   1.00  1.00 .040 .030  1.00         17.00        bal Fe
  26.  442     .20  1.00 .040 .030  1.00  20.50              
  27.  904L    .02  2.00 .045 .035  1.00  21.00  25.50  4.50  Cu 1.50
  28.  17-4PH  .02  2.00 .045 .035  1.00  21.00  25.50  4.50  Cu 1.50
  29.  17-7PH  .02  2.00 .045 .035  1.00  21.00  25.50  4.50  Cu 1.50
  30.  2205    .03  2.00 .030 .020  1.00  22.00   5.50  3.00  0.15N
  31. ------> CAST ALLOYS <------ 
  32.  CA-6NM  .06  1.00 .045 .035  1.00  12.50   4.00  0.70 
  33.  CA-15   .15  1.00            1.50  12.50   1.00      
  34.  CA-40   .40  1.00            1.50  12.50   1.00       
  35.  CB-30   .30  1.00            1.50  20.00   2.00        Ni is max
  36.  CD4MCU  .04  1.00            1.00  25.00   5.00  2.00  Cu 3.0
  37.  CF-3    .03  1.50 .040 .040  2.00  19.00  10.00  
  38.  CF-3M   .03  1.50 .040 .040  1.50  19.00  10.00  2.50 
  39.  CF-8    .08  1.50 .040 .040  2.00  19.00   9.00       
  40.  CF-8C   .08  1.50 .040 .040  2.00  19.50  10.00   
  41.  CF-8M   .08  1.50 .040 .040  1.50  19.50  10.00  2.50 
  42.  CG-8M   .08  1.50 .040 .040  1.50  20.00  10.00  3.50 
  43.  CH-20   .20  1.50 .040 .040  2.00  24.00  13.00       
  44.  CK-20   .20  2.00 .040 .040  2.00  25.00  20.00       
  45.  HF      .30  2.00 .040 .040  2.00  19.00   9.00  0.50 max  C typical
  46.  HH      .35  2.00 .040 .040  2.00  25.00  12.00  0.50 max  C typical
  47.  
  48. ~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~~
  49. NOTE:
  50.  The composition data shown above, and that under "Properties by Alloys
  51.   are for generic identification of the various alloys.  These nominal
  52.   chemistry values, unless indicated as maximum, are the average of the 
  53.   range given in the alloy specifications, and not necessarily typical
  54.   for the specific alloy.
  55.  
  56.  The intent of the above list is to show relative chemistry, alloy by
  57.   alloy, for comparison purposes.  For specific composition ranges, the
  58.   supplier of the stainless steel alloy should be consulted.