  1. Soldering is done at much lower temperatures than brazing, below 800F.
  2.  Principal soldering alloys are a combination of lead and tin.  Tin-antimony
  3.  and tin-silver solders are used for food handling and other applications
  4.  where lead would be objectionable.  Welding has largely replaced soft
  5.  soldering of sheet metal assemblies as shops have become more skilled and
  6.  familiar with welding light gage stainless steel sheet work assemblies.  The
  7.  strength and durability of welded joints is considerably greater than that of
  8.  properly soldered joints.  Nevertheless, soldered joints still find many
  9.  applications in architecture, food processing and plumbing.
  10.  
  11. Sheet metal:  The 300 series stainless steels solder with relative ease
  12.                although types 321 and 316 are somewhat more difficult to
  13.                solder.
  14.  
  15. Surface finish:  Annealed and pickled finishes #1 and #2 or polished surfaces
  16.               #3 and #4 are preferred to the brightly polished surfaces #7
  17.               and #8.  Bright annealed finishes are difficult to solder.
  18.  
  19. Preparation:  Proper cleaning of the surface is the key to tight reliable
  20.                soldered joints.
  21.               1.  Remove all dirt, dust grease, scale, fingerprints, etc.
  22.                    mechanically or with a proven commercial solvent.
  23.               2.  Wipe clean with alcohol or other proven solvent.
  24.               3.  Apply phosphoric acid based flux.
  25.               4.  Tin the surface before assembling the joint.
  26.               5.  Apply solder. See Item F in Joining Menu.
  27.  
  28. Cleaning after soldering:  All flux and solder residue must be removed from the
  29.  surface by scrubbing in water, by chemical cleaning agents, or mechanically,
  30.  or by some combination thereof in order to prevent corrosion in service.  An
  31.  alkaline rinse late in the post-soldering cleaning cycle is very helpful in
  32.  neutralizing acid residues.
  33.  
  34.  
  35. Additional information on brazing stainless steel is available in:
  36.  
  37.      "Welding of Stainless Steels and Other Methods of Joining",
  38.         available from NiDI, Literature Item 9 002.
  39.  
  40.      "Metals Handbook", Ninth Edition, Volume 6, Welding, Brazing
  41.         and Soldering, Metals Park, Ohio  44073.